Abstract Coatings developed through sol-gel method is presented as an interesting replacement to chromium coating. Sol-gel method present advantages as high purity and excellent distribution of the components. The objective of this work is to synthesize and characterize a film obtained by sol-gel route. The film was prepared with 3-(trimethoxysilylpropyl) methacrylate (TMSPMA), tetraethoxysilane (TEOS) and cerium nitrate, using water and ethanol as solvents. Polyethyleneglycol (PEG) plasticizer was added at four different concentrations. The sol was characterized by techniques of viscosity, thermogravimetric analysis (TGA), X-ray diffraction (XRD) nuclear magnetic resonance spectroscopy (NMR) and Fourier transform infrared spectroscopy (FT-IR). The results showed that tetrafunctional alkoxides condensation was retarded by the plasticizer, forming a compact film. The film with 20 g.L-1 of PEG showed the best electrochemical behavior.

Among the applications for protic ionic liquids (PILs), lubrication is one of the newest and the most promising. In this work, ammonium-based protic ionic liquids were tested as lubricant fluids for aluminum-steel contacts. PILs were synthesized with 2-hydroxyethylamine (2HEA) and a carboxylic acid (formic and pentanoic), aiming to understand the effect of two different anion chain lengths on the lubricant behavior. The synthesized PILs were characterized by RMN, FTIR and TGA. Wear tests, conducted using a ball-on-plate configuration, showed that the increase of the anion carbon chain length in the PIL structure reduced significantly the coefficient of friction value. Besides, after the wear tests, the PILs structural integrity was not affected. In the same way, bending under tension (BUT) tests evidenced that the performance for stamping conditions of the PIL with the longest anion carbon chain was similar to that of the commercial lubricant. Since, both formed a uniform tribofilm, developed the same lubrication regime and the drawing forces values were close and constant. Hence, the ionic liquid obtained with 2HEA and pentanoic acid (2HEAPe) is as suitable as the commercial lubricant for metal forming processes.

DIN 1.4110 martensitic stainless steel is largely used in the cutlery industry due to its high corrosion resistance associated with high mechanical resistance. However, when this material works under corrosion and wear conditions at the same time, their synergistic effect can accelerate the degradation process of the alloy. Cryogenic heat treatments have been proposed to improve the dimensional stability and mechanical properties, since they minimize the amount of retained austenite. The aim of this work is to study the effect of deep cryogenic heat treatment at -80 ºC and at -196 ºC on the corrosion resistance and tribocorrosion behavior of DIN 1.4110 martensitic stainless steel. The microstructure, hardness, corrosion resistance and tribocorrosion behavior were evaluated. Although the heat-treated samples presented higher hardness and lower corrosion current density (icorr) compared to samples in spheroidized condition, their material removal under tribocorrosion conditions increased, which demonstrated the synergy between corrosion and wear.

The aim of this work was to study the corrosion behavior of three commercial nanoceramic coatings in comparison to zinc phosphate coatings applied on mild steel (SAE 1010). The coatings were evaluated by scanning electron microscopy (SEM), profilometry and hydrophobicity. The electrochemical behavior was evaluated by dynamic polarization. The results showed that the samples coated with nanoceramics presented contact angles greater than 100º, achieving hydrophobic behavior. Evaluating the electrochemical behavior under dynamic polarization revealed that the nanoceramic coating containing chromium (CHT) exhibited a higher corrosion potential and lower current than the other nanoceramic coatings tested, although its performance in a dilute sodium chloride solution was below that of the zinc phosphate-based coating. Although the nanoceramic coatings exhibited poor electrochemical behavior compared to the zinc-based coatings, they had a higher corrosion resistance when associated with an organic coating.

The present study aimed to create and characterize niobium and niobium-iron 60% coatings applied to steel API 5L X70 using the hypersonic thermal spray process (HVOF). The morphologies of the coatings were analyzed using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and profilometry, while the coatings' hardnesses was evaluated using the Vickers hardness test. The coatings' corrosion resistance was evaluated by monitoring their open circuit potential and potentiodynamic polarization and performing electrochemical impedance spectroscopy in a 0. 05 M NaCl solution. The results showed that the niobium-iron coating contained minor porosity regions, while such defects occurred over large regions of the niobium coating. In terms of corrosion resistance, the coatings obtained in this work promoted a reduction in the substrate's corrosion rate, but the presence of discontinuities such as porosity compromised the barrier effects of these coatings.